PERHITUNGAN LAJU KOROSI PADA MATERIAL BAJA ST 41 AKIBAT PROSES PENGELASAN SMAW (SHIELDED METAL ARC WELDING) DENGAN VARIASI AMPERE 80,120 DAN 3 MEREK EKTRODA

Zhamarsda, Youngga (2020) PERHITUNGAN LAJU KOROSI PADA MATERIAL BAJA ST 41 AKIBAT PROSES PENGELASAN SMAW (SHIELDED METAL ARC WELDING) DENGAN VARIASI AMPERE 80,120 DAN 3 MEREK EKTRODA. Undergraduate thesis, UNIVERSITAS 17 AGUSTUS 1945 SURABAYA.

Preview	Text ABSTRAK.pdf Download (548kB) | Preview
	Text (BAB I) BAB 1.pdf Restricted to Repository staff only Download (11kB)
	Text (BAB II) BAB 2.pdf Restricted to Repository staff only Download (1MB)
Preview	Text (BAB III) BAB 3.pdf Download (16kB) | Preview
	Text (BAB IV) BAB 4.pdf Restricted to Repository staff only Download (622kB)
	Text (BAB V) BAB 5.pdf Restricted to Repository staff only Download (10kB)
Preview	Text LAMPIRAN.pdf Download (936kB) | Preview
	Text JURNAL.pdf Restricted to Repository staff only Download (1MB)
	Text JURNAL TURNITIN.pdf Restricted to Repository staff only Download (808kB)
Preview	Text Teknik_Mesin_1421504716_Imanuel_Maryanto.pdf Download (0B) | Preview

Abstract

Korosi merupakan proses perusakan alami yang terjadi pada material karena pengaruh kondisi sekitar. Korosi tidak dapat dicegah, namun dapat dipercepat atau diperlambat. Eksperimen ini diperuntukkan untuk mengetahui pengaruh proses las smaw terhadap laju korosi pada material baja st 41 d daerah HAZ dan Base Metal dengan variasi ampere 80 dan 120 dengan cara direndam pada larutan Natrium klorida selama 168 jam. . Hasil menunjukkan besar kecil arus pengelasan berpengaruh pada laju korosi di daerah HAZ dan Base Metal pada spesimen, dengan laju korosi terbesar pada Baja ST 41 ampere pngelasan 80 Elektroda Nikko Steel media perendaman Natrium Klorida sebesar 0,004145120 mm/y, dan laju korosi terendah pada Baja ST 41 ampere pengelasan 120 media perendaman Natrium Klorida Elektroda Nikko Steel sebesar 0,0145876 mm/y.